The Study on the Properties of Nylon1010/nano-TiO2 Coating by Flame Spraying

LI Ya-dong1,2，DU Juan4，XIE Bing1，CAO Shao-kui2，WU Zhi-shen3

China Surface Engineering ›› 2005, Vol. 18 ›› Issue (5) : 31-34.

PDF(393 KB)
PDF(393 KB)
China Surface Engineering ›› 2005, Vol. 18 ›› Issue (5) : 31-34.

The Study on the Properties of Nylon1010/nano-TiO2 Coating by Flame Spraying

  • LI Ya-dong1,2，DU Juan4，XIE Bing1，CAO Shao-kui2，WU Zhi-shen3
Author information +
History +

Abstract

The mechanical properties and UV resistance of flame s prayed Nylon1010/nano-TiO2 composite coating were studied. The results showed that when PA1010 was filled with 1.5 % nano- TiO2, the properties of the coating was best. The coating-substrate adhesion strength was 26.4 MPa. The self-strength of the coating was 73.68 MPa. After 240 hours UV radiating, the self-strength of coating was 69.41 MPa. DSC analysis showed that nano-TiO2 can increase the crystallization speed of PA 1010 coating obviously.

Key words

flame spraying；Nylon 1010；nanometer TiO2；coatings；mechanical properties UV resistance

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations
LI Ya-dong1,2，DU Juan4，XIE Bing1，CAO Shao-kui2，WU Zhi-shen3. The Study on the Properties of Nylon1010/nano-TiO2 Coating by Flame Spraying[J]. China Surface Engineering, 2005, 18(5): 31-34
PDF(393 KB)

10

Accesses

0

Citation

Detail
Sections
Recommended
ISSN 1007-9289　CN 11-3905/TG
Supervised by: China Association for Science and Technology
Sponsored by: Chinese Mechanical Engineering Society
Edited and Published by: Editorial Office of China Surface Engineering
Copyright © China Surface Engineering, All Rights Reserved.
Postal Code: 100037　
Tel: (010)88379020/88379056　
E-mail：cse1988@csejournal.com
Visited
Total visitors:　
Visitors of today: 　
Now online:
京ICP备05060958号-2    Powered by Beijing Magtech Co. Ltd,.

/

〈 〉