摘要

利用纳米结构和常规喂料用大气等离子喷涂方法制备了Al2O3/TiO2涂层,研究了水环境中两种涂层与不锈钢对磨时的摩擦磨损性能.结果表明:水环境中,两种涂层摩擦因数变化不大,但是纳米喂料涂层耐磨性能明显优于常规涂层,同时其对偶的磨损率仅为常规涂层对偶磨损率的1/3~1/5,磨损率随载荷的增加不断增加.讨论了水环境中两种涂层的磨损机制.

Abstract

Two types of A1203/TiO2 coating with nano-scale and conventional powders were deposited by plasma spraying. Their wear mechanism against stainless steel as the counterpart of rubbing pair under water environment was discussed. The results showed that the friction coefficients of both coatings are similar at all test loads and exhibit no great difference. However, the coating with nanoscale powders improved wear resistance compared with coating with conventional powders, and also reduced wear rate of the counterpart material.

关键词

摩擦磨损;等离子喷涂;纳米结构;水环境;Al2O3/TiO2涂层

Key words

tribology; plasma spraying; water environment; Al2O3/TiO2 coating

引用本文

导出引用
赵晓琴1,2,周惠娣1,陈建敏1. 水环境中等离子喷涂纳米/微米喂料Al2O3/TiO2涂层的摩擦学行为[J]. 中国表面工程, 2005, 18(5): 35-38
ZHAO Xiao-qin1,2,ZHOU Hui-di1, Chen Jian-min1. Tribological Behaviour of Plasma Sprayed Al2O3/TiO2 Coatings From Nanoscale and Conventional Powders Under Water Environment[J]. China Surface Engineering, 2005, 18(5): 35-38
PDF(293 KB)

8

Accesses

0

Citation

Detail

段落导航
相关文章

/