| Impact of Interface Contact Temperature on the APS Seal Coating |
|
CHEN Zhi-kun, LIU Zi-jing, ZHU Hui-zhao, ZHANG Zhong-cheng
|
|
Guangzhou Research Institute of Nonferrous Metals Research department of new materials, Guangzhou 510650
|
| Abstract: |
| The seal coating were prepared by air plasma spray (APS). The interface contact temperature was adjusted by changing the cooling blast in the spraying process. Optical microscope and scan electron microscope are used to observe the micrograph of the seal coating. The Xray diffraction is used to analyze the phase in the seal coating. The abradable property and antierosion test were performed to investigate the impact of the interface contact temperature on the seal coating property. Results show that plasma spaying seal coating can obtain the typical cellular microstructure. With increasing interface contact temperature, the microhardness, deposit rate, and the antierosion performance are improved; however, the abradablity is reduced. |
| Key words: APS seal coating interface contact temperature deposit rate abradablility antierosion |