文中采用多弧离子镀技术在γ-TiAl合金表面制备了NiCrAlY涂层,用SEM/EDS和XRD等手段研究了该涂层对γ-TiAl合金高温氧化行为的影响。结果表明NiCrAlY涂层在高温下可形成保护性氧化铝膜,显著提高了γ-TiAl的高温氧化抗力。在氧化过程中,NiCrAlY/TiAl涂层体系发生了严重的Ni的内扩散,形成了层状结构的互扩散带。 |
关键词: 多弧离子镀 NiCrAlY γ-TiAl 氧化 互扩散 |
DOI: |
分类号: |
基金项目:国家自然科学基金(50771100) |
|
Effect of Arc Ion PlatedNiCrAlY Coating on Oxidation Behavior of γ-TiAl Alloy |
CHENG Yu-xian, LIU Li, WANG Wen, WANG Fu-hui, WANG Lu1,2
|
1.Shenyang Liming Aeroengine Group Corporation Ltd., AVIC, Shenyang 110043;2.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
|
Abstract: |
NiCrAlY coating was deposited onto γ-TiAl alloy employing arc ion plating and the oxidation behavior was investigated by SEM/EDS and XRD. The results indicated that NiCrAlY coating can remarkably improve the oxidation resistance of γ-TiAl alloy by forming a protective scale. Serious inward diffusion of Ni from the NiCrAlY coating to γ-TiAl substrate was occurred during oxidation,which resulted in the formation of multilayered interdiffusion zone. |
Key words: arc ion plating NiCrAlY γTiAl oxidation interdiffusion |