| 表面润湿性是影响多孔硅实际应用的重要因素，对多孔硅表面润湿性的精确控制是其在生物移植、药物释放等领域实现广泛应用需要解决的关键科学问题之一。文中报道了4种不同孔径大小（10~1 000 nm）、初始润湿性范围从高度亲水（接触角15°）到高度疏水（接触角139°）的多孔硅在氧等离子处理过程中表面润湿性的动态变化过程，发现其润湿性随着处理时间的增长迅速降低至极亲水状态。此外，在主要结果的基础上还拟合了出润湿性变化速率常数与孔径之间的初步规律及经验公式。 |
| 关键词: 多孔硅 润湿性 氧等离子 孔径 |
| DOI：10.3969/j.issn.1007-9289.2013.05.008 |
| 分类号: |
| 基金项目: |
|
| Effects of Oxygen Plasma on Surface Wettability of Porous Silicon |
|
JIANG Lei, LI Zhaomin, YANG Limin, LI Songyan, SUN Qian, ZHANG Dong, WANG Jiqian
|
|
a. State Key Laboratory of Heavy Oil Processing and Center for Bioengineering and Biotechnology, b. College of Petroleum Engineering, China University of Petroleum, Qingdao 266580, Shandong
|
| Abstract: |
| The surface wettability plays an important role in the application of porous silicon. Precisely controlling its surface wettability is one of the key scientific challenges for its further application in the fields such as implantation and drug release. The contact angle changes of four types of porous silicon were measured during the oxygen plasma treatment using a range of samples with pore sizes (101 000 nm) and initial wettability from highly hydrophilic (15°) to highly hydrophobic (139°). It found that the wettability rapidly reduced to extremly hydrophilic state with the growth of processing time. Based on the main observation, the correlation between the wettability change rate constant and the pore size was investigated and an empirical equation was developed. |