| Effects of TiC Coating Prepared by Ion Sputtering with Double Cathodes on Properties of Diamond Tools |
|
LUO Wen1, JIE Xiaohua1, MENG Yunkai2, XU Jiang3, TAO Hongliang2, WEI Jv2
|
|
1. School of Materials and Energy Guangdong University of Technology, Guangzhou 510006; 2. Guangdong MonteBianco Diamond Applications Co., Ltd., Foshan 528313, Guangdong; 3. Department of Material Science and Engineering, NanJing University of Aeronautics and Astronautics Graduate School, Nanjing, 210016
|
| Abstract: |
| TiC coating was prepared on the surface of diamond grains by ion sputtering with double cathodes. The surface morphology, composition of the coating was analyzed by SEM and XRD. The static pressure strength and the impact toughness of the diamond were detected by the static pressure strength tester and the synthetic diamond impact strength tester. The effects of TiC coating on properties of the diamond tools were compared with the uncoated diamond possessing the same grain size and type. The results show that the compact and even TiC coating forms and it grows up in the direction that is perpendicular to the surface of the diamond with the shape of columnar. Owing to the protection of the TiC coating layer, the static pressure strength and thermal stability of the diamond can be improved. The impacting and bending strength of the diamond tools also increase because the existence of TiC coating improves the wetness between the diamond and the tool matrix. |
| Key words: ion sputtering with double cathodes TiC coating diamond |