| 摘要: |
| 对酸性氯化物型化学镀锡的增厚工艺进行了研究.讨论了镀液中Sn2＋浓度、NaH2PO2浓度、（NH2）2CS含量及络合剂B等组分对化学镀沉积速度的影响,并提出了最佳的工艺条件;同时,利用扫描电镜（SEM）和电子能谱（EDS）对镀层表面形貌和镀层成分进行了分析.结果表明：在一定工艺条件下可获得厚度为7.5μm左右的银白色无光化学镀锡层,镀层表面晶粒大小均匀细致,镀层含锡量为95.6%质量分数. |
| 关键词: 化学镀 镀锡 沉积速度 |
| DOI： |
| 分类号: |
| 基金项目: |
|
| Studies on Incrassate Technology of the Electroless Tin Plating in Acid Chloide System |
|
TIAN Wen-zeng，CHEN Bai-zhen，HE Xin-kuai，LIAO Zhou
|
| Abstract: |
| The increassate technology of electroless tin plating in chloride system was studied in this paper. The effect of components concentration on deposition rate were studied, such as Sn2+, NaH2PO2, (NH2)2CS, complex B, and the optimized technology were presented. Besides, the SEM and EDS analyses of surface morphology and deposition layer’s composition were also made. The results showed that the tin deposition coating was silvery white, about 7.5 μm thick ,having fine and compact grains, and containing 95.6 % of w(Sn). |
| Key words: electroless plating tin plating deposition rate |