| 低模量Ti6Al4V表面Ti(Al/Pt)N薄膜强化改性 |
|
孙琳凡1, 时晓光2, 周艳文1, 杜峰1, 司彪1, 郭诚3
|
|
1.辽宁科技大学表面工程研究所 鞍山 114051;2.鞍钢集团钢铁研究院 鞍山 114015;3.鞍钢建设集团有限公司 鞍山 114001
|
|
| 摘要: |
| 为解决硬质薄膜因与软基体硬度和模量差较大导致的薄膜失效问题，提高硬质薄膜在 Ti6Al4V(TC4)钛合金基体上的适应性，使用掺杂氮化钛(TiN)陶瓷薄膜对低模量 Ti6Al4V 合金表面强化。采用热丝增强等离子体磁控溅射技术在 Ti6Al4V 合金表面制备 Ti(Al / Pt)N 薄膜：包括本征 TiN、Al&Pt 掺杂 TiAlN 和 TiAl(Pt)N 薄膜。采用扫描电子显微镜、X-射线衍射仪、 纳米压痕仪、洛氏硬度计和摩擦磨损测试仪分别表征三种薄膜组织形貌、能谱分析、相结构和内应力、纳米硬度和模量及耐磨性。结果表明：Al 元素掺杂使 TiN 薄膜柱状晶细化，截面形貌柱状晶更致密；同时微量 Pt 掺杂后，截面断口呈韧性撕裂。 本征 TiN 和 TiAlN 薄膜衍射峰图谱呈现 TiN(111)取向，TiAl(Pt)N 薄膜的衍射峰呈 TiN(200)主峰位。Al 元素掺杂使 TiN 薄膜晶格畸变增多，内应力从-13 MPa 增大到-115 MPa，导致膜-基结合力恶化，洛氏压痕和摩擦磨损实验中均出现薄膜剥落。Pt 掺杂后薄膜内应力降低到-66 MPa，在洛氏压痕试验中 TiAl(Pt)N 薄膜与基体结合良好，仅有少许环形裂纹。摩擦磨损试验中本征 TiN 和 TiAl(Pt)N 薄膜磨痕较浅，TiAlN 薄膜磨损量最大。Al 元素掺杂细化了 TiN 薄膜柱状晶，但 TiAlN 薄膜内应力大， 耐磨性差、膜-基结合力低。掺杂 Pt 元素后降低了薄膜内应力，提高了韧性与结合力，综合性能最佳。在 Ti6Al4V 合金表面制备 Al&Pt 元素共掺杂 TiN 薄膜，对提高硬质薄膜与软基体变形协调性具有良好应用前景。 |
| 关键词: 热丝增强等离子体磁控溅射 TiN 薄膜 掺杂 结合力 耐磨性 |
| DOI：10.11933/j.issn.1007?9289.20220524004 |
| 分类号:TG156;TB114 |
| 基金项目:国家自然科学基金(51972155，52271056)、辽宁省教育厅基金(LJKZ0278，LJKZ0306)和海洋工程金属材料装备及应用国家重点实验室(HGSKLUSTLN(2020-05))资助项目 |
|
| Strengthening and Modification of Ti(Al / Pt)N Film on the Surface of Low Modulus Ti6Al4V |
|
SUN Linfan1, SHI Xiaoguang2, ZHOU Yanwen1, DU Feng1, SI Biao1, GUO Cheng3
|
|
1.Institute of Surface Engineering, University of Science and Technology Liaoning, Anshan 114051 , China;2.Iron & Steel Research Institute of Angang Group, Anshan 114015 , China;3.Angang Construction Group Co., Ltd, Anshan 114001 , China
|
| Abstract: |
| To solve the problem of film failure caused by the large difference in the hardness and modulus between hard films and soft substrates, and improve the adaptability of hard films on Ti6Al4V (TC4) titanium alloy substrates, doped titanium nitride (TiN) ceramic films are used to strengthen the surface of low modulus Ti6Al4V alloys. Ti(Al / Pt)N films, including intrinsic TiN, TiAlN, and TiAl(Pt)N films, were prepared on the surface of a Ti6Al4V alloy by the hot-wire plasma-enhanced magnetron sputtering technique. The microstructure, composition, phase structure, internal stress, nanohardness and modulus, and wear resistance of the Ti(Al / Pt)N films were characterized by scanning electron microscopy, X-ray diffraction, nano-indentation, Rockwell hardness testing, and friction and wear testing. The results showed that Al doping refined the columnar structure of TiN films, and made the cross-section morphology of columns much more compact. In addition, Al doping increased the critical fracture stress within the film, which reduced the film toughness. Doping with a small amount of metallic Pt enhanced the film toughness, and the fractured section of TiAl(Pt)N exhibited the ductile tearing mode. The diffraction patterns of the intrinsic TiN and TiAlN films showed a TiN (111) orientation. Al atoms replaced the Ti atoms in the TiN lattices and formed a substitutional solid solution of TiN, which widened and weakened the TiN (111) peak. During metallic Pt doping of the TiAlN film, the preferred film orientation changed to the low surface energy (200) of TiN, and the film stress decreased. Al doping increased the distortion of the TiN lattice. The internal stress increased from ?13 MPa of intrinsic TiN to ?115 MPa of TiAlN, which caused the deterioration of the film-to-substrate adhesion. In other words, film spalling occurred in the Rockwell indentation along with friction and wear. Owing to the excellent deformation ability of the metallic Pt element, the addition of Pt to TiAlN helped release the residual stress and enhanced the film toughness; therefore, the internal stress of the film due to Pt doping decreased to ?66 MPa. In the Rockwell indentation experiment, the Ti(Al / Pt)N film was well bonded to the substrate, and only a few annular cracks were observed. In the friction and wear experiments, the wear loss of the TiAlN film was the largest because of the film peeled off, and the wear marks of the TiAl(Pt)N and intrinsic TiN films were very shallow. In short, the TiN films had high hardness and modulus, and were relatively brittle. Because the of the low internal stress of the TiN film, it did not peel off in the indentation detection test, and only edge cracks were observed. The Al-doped TiN film had refined columns, a distorted lattice, and high internal stress. The film peeled off from the TC4 substrate in the Rockwell indentation test. The TiAl(Pt)N film co-doped with Al and Pt showed refined columns, reduced lattice distortion, different orientations, and relatively low internal stress. Cracks appeared at the edge of the indentation, and the film was well bonded to the substrate. The coordination between the Ti(Al / Pt)N film and titanium alloy substrate demonstrated their strong adaptability and good mechanical properties. The Al and Pt co-doped TiN films on the surface of the Ti6Al4V alloy have potential applications in improving the coordinated deformation between hard films and soft substrates. |
| Key words: PEMS TiN film doping adhesion wear resistance |
|
|
|
|