| 摘要: |
| 采用高能离子注渗技术向钢铁零部件表层注渗碳化钨(WC)，碳化钨含量高的富集层厚度0．35mm，碳化钨注渗层总厚度1．2mm。对3种工业产品进行实车对比试验，注渗碳化物的零件的相对耐磨性分别为3．6、3．9、6．25。对离子注渗碳化钨材料的耐磨机理进行分析。 |
| 关键词: 离子注渗 碳化钨 实用效果 耐磨性 |
| DOI： |
| 分类号:TG174.444 |
| 基金项目: |
|
| Analysis of Application and Wear Resistance of the High-energy Ion Implanted WC Coating |
|
ZHAO Tian-lin ZHAO Gang
|
| Abstract: |
| WC was implanted into the surface of steel and iron parts by high-energy ion implanting technique. The implanted coating showed a total thickness of 1.2 mm, while the layer rich of WC had a thickness of 0.35 mm. The real comparing experiments were performed for three kinds of products. The results showed that the relative wear resistance of three WC implanted coatings were 3.6, 3.9 and 6.25 respectively. The wear mechanism of materials with ion implanted WC was discussed |
| Key words: ion implanting,WC,application,wear resistance, |