| 引用本文: | 陈珊珊，樊自拴，孙冬柏，俞宏英，王旭东.气保焊堆焊方法制备的铁基非晶合金涂层[J].中国表面工程,2011,24(3):78~82 |
| CHEN Shan-shan, FAN Zi-shuan, SUN Dong-bai, YU Hong-ying, WANG Xu-dong.Iron Based Amorphous Alloy Coating Prepared by CO2 Welding[J].China Surface Engineering,2011,24(3):78~82 |
|
| 摘要: |
| 以一种多元素铁基合金粉芯丝材（含Fe, Cr, B, Ti, C, Mo等）作为堆焊材料，用CO2气体保护焊堆焊的方法在基体A3钢上制备涂层。用X射线衍射仪检测涂层的晶体结构，DSC分析非晶的起始晶化温度；透射电镜观察涂层的微观组织结构，扫描电镜观察涂层的形貌，并利用显微硬度仪和高温摩擦磨损试验机分别测量涂层的显微硬度和耐磨损性能。结果表明：所制备的涂层均匀致密，与基体结合良好；涂层含有非晶并且非晶的起始晶化温度约为524 ℃；这种非晶涂层具有较高的硬度和很好的耐磨损性能，近表面的最高硬度达825 HV0.3，耐磨性是A3钢的5.9倍. |
| 关键词: 铁基非晶合金 堆焊 涂层 |
| DOI： |
| 分类号: |
| 基金项目: |
|
| Iron Based Amorphous Alloy Coating Prepared by CO2 Welding |
|
CHEN Shan-shan, FAN Zi-shuan, SUN Dong-bai, YU Hong-ying, WANG Xu-dong
|
|
a. Corrosion and Protection Center, Laboratory for CorrosionErosion and Surface Technology b. Beijing Key Laboratory for CorrosionErosion and Surface Technology, University of Science and Technology Beijing, Beijing 100083
|
| Abstract: |
| An iron based powder consisting of Fe, Cr, B, Ti, C, Mo and so on was welded onto A3 steel substrate using CO2 welding to create an amorphous coating. Crystal structure of the coating was studied by XRD, the original crystallization temperature was found via DSC, the microstructure was studied through TEM, the topography of the coatings was observed by SEM and the microhardness and wear resistance were measured using a microhardness tester and a high temperature abrasion machine respectively. The results show that the prepared coatings are even in density and firmly welded to the substrate. The crystallization temperature of the amorphous coating is about 542 ℃. The amorphous coating presents good hardness and wear resistance. The maximum hardness near the surface reaches 825 HV0.3. The wear resistance is 5.9 times than that of the A3 steel. |
| Key words: iron based amorphous alloy welding coating |