| 摘要: |
| 为使AlSi20%Al/Ni超音速等离子喷涂涂层获得优良的结合性能，采用正交实验法研究了喷涂距离、喷涂电压、喷涂电流等喷涂工艺参数对结合强度的影响。利用X射线衍射、扫描电镜等手段对涂层的相组成和断口形貌进行分析，利用WDWE100D微机控制式万能拉伸试验机对涂层结合强度进行测试。结果表明：涂层由AlSi和AlNi两相组成，影响AlSi20%Al/Ni涂层结合强度工艺参数的主次顺序为喷涂距离、喷涂电压、喷涂电流，优化后的工艺参数为主气流量3.2 m3/h，喷涂电流为380 A，喷涂电压为130 V，喷涂距离为90 mm，在此参数下制备的涂层组织致密，其结合强度为65.5 MPa。 |
| 关键词: 超音速等离子喷涂 AlSi20%Al/Ni涂层 工艺参数 结合强度 正交实验 |
| DOI： |
| 分类号: |
| 基金项目: |
|
| Influence of Supersonic Plasma Spraying Process on Bonding Strength of AlSi20%Al/Ni Coating |
|
FAN Wen–chao， TAN Jun，WANG Hai–jun， LIU Ming， LI Xu–qiang
|
|
a. Science and Technology on Remanufacturing Laboratory b. Key Laboratory for Surface Engineering, Academy of Armored Force Engineering, Beijing 100072
|
| Abstract: |
| In order to get a supersonic plasma sprayed AlSi20%Al/Ni coating with good properties, the effect of supersonic plasma spraying process parameters on the bonding strength of the coatings was investigated by orthogonal experiment. The fracture of the coating and morphology of the sprayed layer were investigated by Xray diffraction(XRD) and scanning electron microscopy(SEM), and the bonding strength of the coatings was tested by WDWE100D. The result shows that the coating is composed by AlSi and AlNi, the primary and secondary gradation of process parameters which are effect on the bonding strength of the coating are spraying distance, spraying voltage and spraying electric current. The optimized process parameters of the supersonic plasma spraying AlSi20%Al/Ni coating is primary gas flux 3.2 m3/h, spray current 380 A, spray voltage 130 V and spray distance 90 mm. With the optimized process parameters, the coating is compact and the bonding strength of the coating reaches to 65.5 MPa. |
| Key words: supersonic plasma spraying AlSi20%Al/Ni coating process parameters bonding strength orthogonal experiment |