镁合金表面激光制备镍铝青铜涂层
李 岩a，王文先a,b，崔泽琴a，张亚楠a，许并社a,b
太原理工大学 a. 材料科学与工程学院 b. 新材料界面科学与工程省部共建教育部重点实验室
摘要:
利用激光熔覆的方法在AZ31B镁合金表面制备镍铝青铜涂层，采用扫描电镜、X射线衍射仪和显微硬度仪对涂层的微观形貌、物相以及显微硬度进行分析，采用PS–168A型电化学测量系统对涂层以及母材进行电化学腐蚀性能测试。结果表明，涂层内白色基体上析出富Cr的玫瑰状和块状的K相，涂层的物相主要由FeAl3、Al3Ni、Ni、Cu、Cr等组成，涂层的显微硬度最高可达602 HV0.2，较母材的50 HV0.2提高了约11倍，涂层的腐蚀电位?1.02 V较母材的?1.49 V提高了0.47 V。
关键词:  镁合金  激光熔覆  镍铝青铜
DOI：
分类号:
基金项目:山西省自然科学基金资助项目（2008011044）
Nickel Aluminum Bronze Coating on the Surface of Magnesium Alloy Prepared by Laser Cladding
LI Yana, WANG Wen–xiana,b, CUI Ze–qina, ZHANG Ya–nana, XU Bing–shea,b
a. College of Material Science and Engineering b. China Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology
Abstract:
The nickel aluminum bronze coating was prepared on AZ31B magnesium alloy by laser cladding, The morphology, phase and microhardness of the coatings were analyzed by scanning electron microscopy (SEM), X–ray diffraction and Microhardness tester, the electrochemical corrosion of the coatings and base metal were tested by PS–168A type electrochemical measuring system. The results show that Cr–rich Rose–like and nubby K–phase are precipitated on white matrix structure, the main phases of coating consist of FeAl3, Al3Ni, Ni, Cu and Cr, the maximum microhardness is up to 602 HV0.2, 11 times higher than the base metal(50 HV0.2). Moreover, the corrosion potential of coating is ?1.02 V, increased 0.47 V compared with the base metal.
Key words:  magnesium alloy  laser cladding  nickel aluminum bronze