引用本文:李文亚,陈亮,余敏,郭学平,Hanlin Liao.热处理对冷喷涂Fe涂层组织与性能影响研究[J].中国表面工程,2010,(2):90~94
LI Wen–ya, CHEN Liang, YU Min, GUO Xue–ping, LIAO Han–lin.Effect of Heat Treatment on Microstructure and Properties of Cold Sprayed Iron Coating[J].China Surface Engineering,2010,(2):90~94
【打印本页】   【HTML】   【下载PDF全文】   【查看/发表评论】  【EndNote】   【RefMan】   【BibTex】
←前一篇|后一篇→ 过刊浏览    高级检索
本文已被：浏览 2944次   下载 1919次 本文二维码信息
码上扫一扫！
分享到： 微信 更多
字体:加大+|默认|缩小-
热处理对冷喷涂Fe涂层组织与性能影响研究
李文亚,陈亮,余敏,郭学平,Hanlin Liao1,2
1. 西北工业大学 摩擦焊接陕西省重点实验室, 西安 710072;2. LERMPS, Université de Technologie de Belfort– Montbéliard, Site de Sévenans, Belfort 90010, France
摘要:
冷喷涂作为一种新型的涂层技术，在制备大部分金属涂层、金属陶瓷复合涂层方面有着巨大的潜力。本文采用冷喷涂在Al基体上制备了Fe涂层，并结合喷涂后热处理研究了涂层组织与性能特点。结果表明，所得Fe涂层的内部组织比较致密；受到喷涂过程中空气的影响，喷涂射流呈现亮流，所制备涂层表面有较大、较深气孔。在较低温度下热处理后Fe涂层的显微组织变化不明显，显微硬度明显降低；Fe涂层与Al基体之间形成约10 μm厚度的金属间化合物层。
关键词:  冷喷涂  真空热处理  Fe涂层  显微组织  显微硬度
DOI：
分类号:
基金项目:西北工业大学翱翔之星计划，教育部新世纪优秀人才计划(NCET–08–0463)
Effect of Heat Treatment on Microstructure and Properties of Cold Sprayed Iron Coating
LI Wen–ya, CHEN Liang, YU Min, GUO Xue–ping, LIAO Han–lin1,2
1. Shannxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xi’an 710072;2. LERMPS, Université de Technologie de Belfort–Montbéliard, Site de Sévenans, 90010 Belfort Cedex, France
Abstract:
Cold spraying has great potentials in deposition of a majority of metallic coatings and metal–ceramic composites for many industry applications. In this study, iron coatings were deposited on aluminum substrates and the effect of post–spray heat treatment on the coating microstructure and microhardness was examined. The results showe that the as–sprayed Fe coating presents a relatively dense inner structure but a relatively porous top layer. Some large open pores were present on the coating surface due to the influence of in–flight particle surface oxidation which was observed as the bright spray jet during spraying. The microstructure of the annealed Fe coating changed little, but the coating microhardness was decreased significantly. The intermetallics of 10μm thickness were formed between the Fe coating and Al substrate.
Key words:  cold spraying  vacuum heat treatment  Fe coating  microstructure  microhardness